PA66 AKV 50 H3.0 000000德國朗盛Durethan 50%玻纖熱老化穩定注塑尼龍66塑料（18024445500）

PA 66, 50 % glass fibers, injection molding, heat-aging stabilized



ISO Shortname: ISO 1874-PA 66, GHR, 14-160, GF50

Property Test Condition Unit Standard guide value
d.a.m. cond.
Rheological properties
C Molding shrinkage, parallel 60x60x2; 300 °C / MT 80 °C; 600 bar % ISO 294-4 0.37　
C Molding shrinkage, transverse 60x60x2; 300 °C / MT 80 °C; 600 bar % ISO 294-4 0.93　
Post- shrinkage, parallel 60x60x2; 120 °C; 4 h % ISO 294-4 0.05　
Post- shrinkage, transverse 60x60x2; 120 °C; 4 h % ISO 294-4 0.09　

Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus 1 mm/min MPa ISO 527-1,-2 16000　
C Tensile Stress at break 5 mm/min MPa ISO 527-1,-2 230　
C Tensile Strain at break 5 mm/min % ISO 527-1,-2 2.5　
C Charpy impact strength 23 °C kJ/m² ISO 179-1eU 100　
C Charpy impact strength -30 °C kJ/m² ISO 179-1eU 100　
C Charpy notched impact strength 23 °C kJ/m² ISO 179-1eA 17　
C Charpy notched impact strength -30 °C kJ/m² ISO 179-1eA 15　
Charpy notched impact strength -40 °C kJ/m² ISO 179-1eA 14　
Izod impact strength 23 °C kJ/m² ISO 180-1U 90　
Izod impact strength -30 °C kJ/m² ISO 180-1U 90　
Izod notched impact strength 23 °C kJ/m² ISO 180-1A 15　
Izod notched impact strength -30 °C kJ/m² ISO 180-1A 13　
Flexural modulus 2 mm/min MPa ISO 178-A 15300　
Flexural strength 2 mm/min MPa ISO 178-A 360　
Flexural strain at flexural strength 2 mm/min % ISO 178-A 3.0